rtv silicone rubber for architectural stone mold
Â
Main applications on  architectural stone mold products making liquid molding silicone rubber material is mainly used for making molds for duplications for the industries such as Poly resin, epoxy poly-resin, plaster crafts, soap crafts, candles crafts, lighting, architectural decorations, embossed furnitures, plastic toys, gifts and stationeries, large statues.
Â
Features of stone products making liquid molding silicone rubber material wholesale are low viscosity, good fluidity, high tensile and tear strength, produced by molds can be used repeatedly, longer life expectancy.
Â
Operations on stone products making liquid molding silicone rubber material :
(1) Mixing:RTV-2 silicone rubber is a kind of flowing liquid and it contains two parts. Part A is a kind of white flowing liquid and part B is the curing agent. Remember to mix part A and part B completely, otherwise the silicon rubber will be partially solidified and this will give birth to difficulties in your final operation. What's more, the finished moulds will meet a short life. All of these will cause a waste of silicon rubber.
Â
(2) Vacuum pumping: After finishing the first step, then go to the vacuum pumping . Usually, there will be some air bubbles in the mixture during the mixing process working. So after the first step after finishing handling of the original mold, we need come to the vacuum pumping process.This step is better for taking less than 3-5 minutes. Otherwise, it will cause cross linking reaction, and no more further steps will be available.
Â
(3) Brushing cast or Perfusion Molding operation
a.Carefully wash the original mold , then dry it with an air gun. Then brush some release agent such as soap water, detergent,vaseline,liquid wax ,etc..
b. Evenly brush the mixed silicon rubber on the product which is covered with mold spray with a brush or a brush pen.
c. After the cross linking reaction (about 30 minutes), brush a second coat which can increase the tension and tear strength of the mold.
d. Cover a glass cloth on it after another 30 minutes of a second cross linking reaction, and use a brush pen or a brush to avoid any interstices.
e. Cover a third coat.
(Note:Â if you have high requirements for the tension and the tear strength for the mold, please repeat step c and step d. Hence, the finished silicone moulds will have a good quality and a longer life, which can help you save cost and increase production efficiency.)
(4)Operations for the external mold:
a. Make a square frame with four pieces of wooden boards or rubber plates, then place the product which is covered with the finished silicon rubber mould in the middle.
b. Slowly and evenly perfuse the gypsum into the square frame. Also you can brush the resin on the product which is covered with the finished silicon rubber mould with a brush or a brush pen. Repeat this process two or three time after the cross link reaction.
(5) Pouring moulding:
It is suitable for simple products with the smooth surface. Without any mold lines, which helps you save time and is easy for operation. Evenly and slowly perfuse the mixed silicone rubber into the square fram. After the cross linking reaction and the silicone rubber turns dry,you can take the products out. Thus, the mold has been done.
(Note:we usaully use soft silicone rubber to make molds by perfusing, which is easy for demoulding and will not damage the product in the silicone molds.)
Datasheet:
Model |
E-630# |
Appearance |
TRANSLUCENT |
MIXING RATIO |
1:1 |
Operating time (mins 25 0C ) |
20-40 |
Curing time(hours 25 0C) |
3-5 |
Hardness (A°) |
30±2 |
Density ( g/cm 3 ) |
1.08 |
Viscosity (Mpas -25 0C) |
15000 |
Tensile-strength(kgf /cm2 ) |
≥40 |
Tear-strength (kgf /cm ) |
≥30 |
Elongation-break(%) |
≥ 450 |
Retractility(%) |
≤0.1 |
Operation instruction  :
1. Pls clear the model and tool totally before operation to prevent cure inhibition.
2.Weigh the two part correctly by electronic weight in two separate container .
3. Mixing the two part in 1:1/10:1 and stir part A and part B evenly in 2-3 minutes .
4.And get the mixture for vacuum-pumping for de-air the bubble in around 2-3
minutes . (If there is no vacuum machine, pls pour the mixture carefully and slowly
down the side of the mold frame so that less bubbles caused)
5. Enclose the product (the original model) with four plastic plates or wooden plates.
6. Clean your products and brush a layer of release agent(detergent or soap water) on
your product.
7. Pour the vacuumed mixture into the model frame from the side of the mold frame .
More information , pls feel free to contact Ms Hebbe:
 Mob:+8618938861889
Â
Â
rtv silicone rubber for architectural stone mold
Â
Main applications on  architectural stone mold products making liquid molding silicone rubber material is mainly used for making molds for duplications for the industries such as Poly resin, epoxy poly-resin, plaster crafts, soap crafts, candles crafts, lighting, architectural decorations, embossed furnitures, plastic toys, gifts and stationeries, large statues.
Â
Features of stone products making liquid molding silicone rubber material wholesale are low viscosity, good fluidity, high tensile and tear strength, produced by molds can be used repeatedly, longer life expectancy.
Â
Operations on stone products making liquid molding silicone rubber material :
(1) Mixing:RTV-2 silicone rubber is a kind of flowing liquid and it contains two parts. Part A is a kind of white flowing liquid and part B is the curing agent. Remember to mix part A and part B completely, otherwise the silicon rubber will be partially solidified and this will give birth to difficulties in your final operation. What's more, the finished moulds will meet a short life. All of these will cause a waste of silicon rubber.
Â
(2) Vacuum pumping: After finishing the first step, then go to the vacuum pumping . Usually, there will be some air bubbles in the mixture during the mixing process working. So after the first step after finishing handling of the original mold, we need come to the vacuum pumping process.This step is better for taking less than 3-5 minutes. Otherwise, it will cause cross linking reaction, and no more further steps will be available.
Â
(3) Brushing cast or Perfusion Molding operation
a.Carefully wash the original mold , then dry it with an air gun. Then brush some release agent such as soap water, detergent,vaseline,liquid wax ,etc..
b. Evenly brush the mixed silicon rubber on the product which is covered with mold spray with a brush or a brush pen.
c. After the cross linking reaction (about 30 minutes), brush a second coat which can increase the tension and tear strength of the mold.
d. Cover a glass cloth on it after another 30 minutes of a second cross linking reaction, and use a brush pen or a brush to avoid any interstices.
e. Cover a third coat.
(Note:Â if you have high requirements for the tension and the tear strength for the mold, please repeat step c and step d. Hence, the finished silicone moulds will have a good quality and a longer life, which can help you save cost and increase production efficiency.)
(4)Operations for the external mold:
a. Make a square frame with four pieces of wooden boards or rubber plates, then place the product which is covered with the finished silicon rubber mould in the middle.
b. Slowly and evenly perfuse the gypsum into the square frame. Also you can brush the resin on the product which is covered with the finished silicon rubber mould with a brush or a brush pen. Repeat this process two or three time after the cross link reaction.
(5) Pouring moulding:
It is suitable for simple products with the smooth surface. Without any mold lines, which helps you save time and is easy for operation. Evenly and slowly perfuse the mixed silicone rubber into the square fram. After the cross linking reaction and the silicone rubber turns dry,you can take the products out. Thus, the mold has been done.
(Note:we usaully use soft silicone rubber to make molds by perfusing, which is easy for demoulding and will not damage the product in the silicone molds.)
Datasheet:
Model |
E-630# |
Appearance |
TRANSLUCENT |
MIXING RATIO |
1:1 |
Operating time (mins 25 0C ) |
20-40 |
Curing time(hours 25 0C) |
3-5 |
Hardness (A°) |
30±2 |
Density ( g/cm 3 ) |
1.08 |
Viscosity (Mpas -25 0C) |
15000 |
Tensile-strength(kgf /cm2 ) |
≥40 |
Tear-strength (kgf /cm ) |
≥30 |
Elongation-break(%) |
≥ 450 |
Retractility(%) |
≤0.1 |
Operation instruction  :
1. Pls clear the model and tool totally before operation to prevent cure inhibition.
2.Weigh the two part correctly by electronic weight in two separate container .
3. Mixing the two part in 1:1/10:1 and stir part A and part B evenly in 2-3 minutes .
4.And get the mixture for vacuum-pumping for de-air the bubble in around 2-3
minutes . (If there is no vacuum machine, pls pour the mixture carefully and slowly
down the side of the mold frame so that less bubbles caused)
5. Enclose the product (the original model) with four plastic plates or wooden plates.
6. Clean your products and brush a layer of release agent(detergent or soap water) on
your product.
7. Pour the vacuumed mixture into the model frame from the side of the mold frame .
More information , pls feel free to contact Ms Hebbe:
 Mob:+8618938861889
Â
Â
Arrow Magnetic Welding Holder,Magnetic Tray,Car Seat Cushion,Multi-Purpose Welding Tool Kit
SHAOXING SINO IMPORT & EXPORT CO.,LTD , https://www.sxsmarto.com